Hot Sealing Adhesive Film For Foam
High strength foam sealing adhesive film is suitable for a wide range of foam materials, including EVA, PU sponge, XPE/IXPE foam, EPE pearl cotton, closed-cell foam, rubber-plastic foam, and memory foam. It performs well in both soft and rigid foam lamination applications...
- Fast Delievery
- Quality Assurance
- 24/7 Customer Service
Product Introduction
Introduction
Hot melt adhesive film for foam bonding is widely suitable for various foam materials, including EVA foam, PU sponge, XPE/IXPE cross-linked foam, EPE pearl cotton, closed-cell foam, rubber-plastic foam, and slow-rebound memory foam. It works perfectly for both soft and rigid foam lamination.
Our EVA,TPU,PE,PP hot melt adhesive film all can bonding it.
Technical Parameters
WT-106 EVA hot melt adhesive film
Product Composition：
EVA Copolymer+Tackifying resin+Accessories
Product Performance Index：
Appearance Semi-Transparent Granules
Softening Point(Ring and Ball) 85±5℃
Viscosity (175℃) 8±5Pa.s
Product Packaging：
25Kg/Bag,inside plastic bag,outside Woven bag
Products Description
No Corrosion to Foam
Solvent-free formula, no foam burning, no hardening, no shrinkage or deformation. It effectively avoids material damage caused by traditional liquid glue.
Smooth Lamination Without Bubbles
Uniform adhesive layer by full-surface hot pressing, no wrinkling, no glue overflow, and flat bonding appearance.
Flexible and Foldable
The Thermoplastic adhesive film for foam materials itself has excellent elasticity. It will not crack or delaminate during bending, stamping and die-cutting, matching the soft characteristics of foam.
Eco-friendly & Odorless
Zero VOC, no formaldehyde, safe for packaging, interior decoration, home textiles and children's products.
Simple Production Process
The Foam composite hot melt adhesive film is compatible with automatic hot pressing, roll lamination and sheet bonding. Save drying time and greatly improve production efficiency.
Product Applications
The Solvent-free foam bonding hot melt film can be used for plastic, fiber fabric, metal, wood, ceramics and other materials bonding. Widely used in the clothing industry decals, labels, automotive industry interior parts, electronics industry, packaging industry, communication industry and so on.
Instructions:
We suggest The operating temperature for adhesive granules is 130-180 ℃ . The surface of the material should be dry and clean without oil.
Storage
Storage condition: store in cool and dry condition.
Shelf life is one year
WT-923T HOT MELT ADHESIVE FILM
Product Composition
100% Polyurethane Resin
Product Performance Index
|
Appearance |
Transparent film |
|
Softening Point(Ring and Ball) |
138±5℃ |
|
Initial flow temperature |
120℃ |
|
Viscosity Range(190℃) |
90000-100000.mpa.s |
Specification
The thickness of the regular hot melt adhesive film:
WT-923T-1 0.01mm
WT-923T-1.5 0.015mm
WT-923T-2 0.02mm
WT-923T-3 0.03mm
The regular width: 156cm or we can customized the width by your request
Product Packaging
500M/Roll,Woven bags lined with plastic bags or Carton
Product Usage
It is mainly used for bonding the polyester film, garment fabric, leather, PVC & PU synthetic leather. It also can be used for fiber fabric, plastic, metal, wood, ceramic and other materials' bonding and laminating.
六,Product Operation Instructions
Operating temperature is 150-180 ℃ . The surface of the material to be bonded should be dry and clean without oil stain. If it is necessary, t he objects to be bonded should be roughening.
Place the film onto the object to be bonded. Heat it to above the melting temperature, press it properly, tear off the release paper, heat it to above the melting temperature, then laminating the other side bonding surface, press it properly, and cure instantly in cooling to complete the bonding.